بررسی و مقایسه تاثیر عملیات حرارتی بر خواص پوشش NiCrBSi اعمال شده به دو روش HVOF و HP/HVOF بر فولاد زنگ نزن 316

STUDENT

DEGREE

YEAR

Nickel-based coatings are one of the conventional coatings that deposited on parts that exposed to extreme wear. One of these coatings is the NiCrBSi alloy. In this study the effect of heat treatment on microstructure, hardness and tribological behavior of the HP/HVOF sprayed NiCrBSi on 316 stainless steel analyzed. The results obtained by metallographic, hardness and abrasion tests indicate that the hardness of coating increases from 200 to 650 Vickers. In addition, the coating increases the wear resistance of the specimens. Heat treatment of the coatings at 950 and 1000 ° C for one hour reduce the porosity, hardness and increase the wear resistance of specimens. Keywords : Thermal spray, Nickel based coating, Heat treatment, Wear.

یکی از پوشش های متدوال بر روی قطعاتی که در معرض سایش شدید قرار می گیرند، پوششهای پایه نیکل می باشند. آلیاژ NiCrBSi نمونه ای از این پوشش ها می باشد. در این پژوهش تاثیر عملیات حرارتی بر ساختار، سختی و رفتار تریبولوژیکی این پوشش که بر روی فولاد زنگ نزن 316 با استفاده از فرایند HVOF فشار بالا اعمال شده، مورد بررسی قرار گرفته است. نتایج بدست آمده توسط آزمون های متالوگرافی، سختی سنجی و سایش حاکی از آن است که اعمال پوشش باعث افزایش سختی زیرلایه از 200 به 650 ویکرز شده است. علاوه بر آن، پوشش دهی باعث افزایش مقاومت به سایش نمونه ها گردیده است. انجام عملیات حرارتی در دماهای 950 و 1000 درجه سانتیگراد به مدت یک ساعت باعث کاهش میزان تخلخل و سختی و همچنین افزایش مقاومت به سایش نسبت به نمونه hy; بدون عملیات حرارتی گردیده است.