Evaluation of the Mechanism and Effect of Gold Nanometer Coating on Laser Interaction with Aluminum Surface
: In this thesis, formation of uniform and large-area micro/nanostructures on pure aluminum surfaces using a continuous-wave laser irradiation is presented. Gold nanolayer coating was utilized as a confinement layer for controlling the possible hydrodynamic phenomena in a molten area. Dependency of the laser-induced morphology on the thickness of a gold coating was investigated in this regard. Results showed that the formation of uniform structures of average sizes of 50 nm-5µm on aluminum surface was possible following the irradiation of a continuous-wave CO 2 laser, delivering 130 W beam power. Alterations of the surface morphology brought about an increase in specific absorption peaks at the UV region and the appearance of an absorption peak in the visible range. In addition, these structure-covered surfaces provided interesting reflection behaviors in different spectral areas, which can clearly reflect their high potential to be used as selective solar absorber
اصلاح سطح توسط لیزر یکی از موضوعات تحقیقاتی چالش برانگیز در سال‌های اخیر است. اصلاح سطح توسط لیزر، روشی تک مرحله ای، سازگار با محیط زیست، بدون تماس با سطح ماده و قابل کاربرد برای مواد مختلف به خصوص فلزات است. هزینه‌بر بودن اصلاح سطوح توسط لیزرهای آزمایشگاهی و نقطه ای بودن منطقه اصلاح شده، دو مشکل اساسی در این زمینه است. مطالعات انجام شده نشان داده است که اعمال پوشش نانوضخامت طلا بر روی زیرلایه‌های فلزی توانسته است تاثیر قابل ملاحضه‌ای در اندرکنش لیزر با زیر لایه داشته باشد. بر همین اساس، در این پژوهش سعی شده است اثرات پوشش‌های نانوضخامت طلا در اندرکنش لیزر با زیرلایه آلومینیوم خالص مورد بررسی قرار گیرد.